SLOVÁK Petr Palacky University in Olomouc

Spoluautoři SOUKUPOVÁ Jana, KAŠLÍK Josef, NOVÁK Petr, FILIP Jan, ZBOŘIL Radek, ČERNÍK Miroslav
Spolupracující instituce: Technical University of Liberec, Liberec, Czech Republic, EU

Aging of surface-modified nanoscale zero-valent iron (nZVI) particles represents one of the key limiting factors in their usage for remediation of polluted sites. We investigated a short-term aging process of nZVI particles stabilized with 4 nm thin iron oxide shell (Nanofer STAR from NANO IRON, s.r.o.). Dense suspension (20 wt.%) of Nanofer STAR was prepared using homogenization of powdered particles in either water or sodium carboxymethyl cellulose (CMC) solution and stored at either room temperature or at approx. 6°C. Morphological changes (TEM), surface area (BET), phase transformations (XRD, Mössbauer spectroscopy) and impact on Cu2+ removal were monitored after 8, 24 and 48 hours of aging. The results showed partial degradation of the protective shell after 48 hours of aging in both aqueous and CMC-containing suspension at room temperature. It was accompanied with the increase of surface area of vacuum dried samples (from 10 – 15 to 30 m2•g−1). However, these effects were fairly suppressed at lower temperature in both media. Phase composition changes caused by aging were under limit of detection. Six times higher removal of Cu2+ was achieved with 48 hours-aged Nanofer STAR (water, room temperature) than with the freshly homogenized suspension. Such dramatic increase in the removal efficiency was observed also with CMC modified Nanofer STAR suspension aged for 24 hours at room temperature. As Nanofer STAR is being used for the site remediation in pilot scale at various localities worldwide, these observations should be taken into account in order to achieve highest possible removal efficiency. ACKNOWLEDGEMENT: The authors gratefully acknowledge the support by Technology Agency of the Czech Republic "Competence Centres" (project TE01020218) and the Operational Program Education for Competitiveness - European Social Fund (CZ.1.07/2.3.00/20.0155). This work was further supported by Student Projects IGA_PrF_2014023 and IGA_PrF_2014017 of Palacký University. The authors would like to thank Mgr. Jana Stráská for measurements on transmission electron microscope.