ŚWIĘTEK Małgorzata AGH University of Science And Technology

Spoluautoři KOZIEŁ Agata, TOKARZ Waldemar, TARASIUK Jacek, WROŃSKI Sebastian, BŁAŻEWICZ Marta

3-D porous biodegradable polymer nanocomposites are widely used as scaffolds in bone regenerative medicine. Incorporation of magnetic particles into polymer matrix enables to create useful tool, which in the presence of external magnetic field, would stimulate and accelerate regeneration process [1]. Carbon nanotubes, because of their excellent mechanical properties, are a popular reinforcement of polymer nanocomposites [2]. The aim of these studies was to prepare and characterize a novel polymer nanocomposite with magnetic properties. For this purpose, carbon nanotubes-iron oxide hybrid nanoparticles were used as a nanoaddition and a biodegradable poly(ε-caprolactone) polymer served as a matrix. Percentage content of the hybrid particles was 1% with respect to polymer weight. 3-D porous scaffolds were fabricated using solvent casting/particulate leaching method. As a porogen, sodium chloride was used. Prepared materials were characterized using micro-Computed Tomography (μ-CT), scanning electron microscopy (SEM), Zwick testing machine and Vibrating Sample Magnetometer. . Performed experiments revealed presence of pores in two fractions of sizes: large, corresponding to the shape and size of salt’s grains, as proven by the μ-CT, and smaller pores, visualized by the microscopic observations. Additionally, presence of assorted agglomerates was observed, with sizes inversely proportional to their number. Magnetic measurements indicated that both the nanoaddition and the polymer nanocomposites possess superparamagnetic properties. Compared with pure poly(ε-caprolactone) scaffold, slight increase of the Young’s moduli was observed. Thus, the conducted studies proved that the introduction of hybrid particles into polymer matrix allows obtaining magnetic nanocomposites with improved mechanical properties. ACKNOWLEDGEMENTS: This research has been supported by the National Center of Science (NCN) under grant: UMO-011/01/B/ST5/06424 LITERATURE: [1] SINGH, R.K., PATEL, K.D., LEE, E.-J., KIM, J-H., KIM, T.-H., KIM, H-W., Potential of Magnetic Nanofiber Scaffolds with Mechanical and Biological Properties Applicable for Bone Regeneration, PLoS ONE 9(4): e91584 [2] SPITALSKY, Z. TASIS, D., PAPAGELIS, K., GALIOTIS, C., CAffect Carbon nanotube-polymer composites: Chemistry, processing, mechanical and electrical properties, Progress in Polymer Science 35, 2010, 357-401