ZEMAN Tomáš University of Defence

Spoluautoři DOČEKAL Bohumil, MIKUŠKA Pavel, BUCHTOVÁ Marcela, MÍŠEK Ivan, ŠERÝ Omar, VEČEŘA Zbyněk

Results of the statistical analysis of a long-term inhalation experiment on laboratory mice are presented. During 17 weeks of the experiment, the experimental group was exposed to inhaled manganese oxides nanoparticles. Manganese oxides (MnO.Mn2O3) nanoparticles (MnONPs) were synthesized continuously via aerosol route in a hot wall tube flow reactor using a thermal decomposition of metal organic precursor manganese(II)acetylacetonate in the flow tube reactor (in vertical position) at temperature 750 °C in the presence of 30 vol% of oxygen. The concentration of produced MnONPs at the reactor output was in the range 1-3 × 107 particles/cm3 and the size of generated nanoparticles MnO.Mn2O3 was in the range 7-50 nm. Before entering the inhalation chamber, MnONPs in the mixture of N2, O2 and air (at total flow rate of 3 L/min) were further diluted using filtrated humidified air (at flow rate up to 60 L/min) at temperature 21 °C resulting in the MnONPs concentration 5 × 105-2 × 106 particles/cm3. At regular time intervals the mass of selected internal organs of mice from both experimental and control group was assessed. It has been proven that inhaled nanoparticles are able to influence the mass of internal organs of mice. Statistically significantly lower mass of kidneys, liver and spleen and higher mass of pancreas have been found in the experimental group compared to the control group.